Please consider attending the following: MATERIALS ENGINEERING SEMINAR "Effects on Rheology and Hydration of the Addition of Cellulose Nanocrystals (CNC) in Portland Cement Pastes" By Francisco J. Montes Purdue MSE Ph.D. Final Exam Advisor: Professor Jeffery P. Youngblood ABSTRACT Cellulose Nanocrystals have been used in a wide range of applications including cement composites as a strength enhancer. This work analyses the use of CNC from several sources and production methods, and their effects on rheology and hydration of pastes made using different cement types with different compositions. Cement Types I/II and V were used to prepare pastes with different water to cement ratios (w/c) and measure the changes in rheology upon CNC addition. The presence of Tricalcium Aluminate (cement chemistry denotes as C3A) played an important role in the magnitude of CNC effects. At dosages under 0.5vol% relative to dry cement, CNC reduced the yield stress up to 50% the control value. Pastes with more C3A reduced yield stress over a wider range of CNC dosages. CNC also increased yield stress of pastes with dosages above 0.5%, twice the control value for pastes with high C¡A content at 1.5% CNC and up to 20 times for pastes without C¡A at the same dosage. All the CNCs used were characterized in length, aspect ratio, zeta potential to identify a definitive factor that governs the effect in the rheology of cement pastes. However, no definitive evidence was found that any of these characteristics dominated the measured effects. The CNC dosage at which the maximum yield stress reduction occurred increased with the amount of water used in the paste preparation, which evidences the dominance of the water to cement ratio in the rheological impact of CNC. Isothermal calorimetry showed that CNC cause concerning retardation effects in cement hydration. CNC slurries were then tested for sugars and other carbohydrates that could cause the aforementioned effect, then slurries were filtered, and impurities were detected in the filtrate, these impurities were quantified and characterized, however, the retardation appeared to be unaffected by the amount of the species detected, suggesting that the crystal chemistry, consequence of the CNC processing method, is responsible of this retardation. This work explores the benefits and drawbacks of the use of CNC in cement composites by individually approaching rheology and hydration on a range of physical and chemical conditions to build a better understanding of the observed effects can be achieved. Understanding the effect of CNCs on cement paste rheology can provide insights for future work of CNCs applications in cement composites. Date: Tuesday, November 27, 2018 Time: 1:30 P.M. Place: ARMS PGSC-105AB