Dear all, I invite you for some free food, snacks and coffee on the occasion of my final defense examination. The details are as given below. Regards, Sambit Date: Friday, May 30th Time: 10:00 AM Location: Birck 1001 Title: Charging and Breakdown in Amorphous Dielectrics: Phenomenological Modeling Approach and Applications Abstract: Amorphous dielectrics of different thicknesses (nm to mm) are used in various applications. Low temperature processing/deposition of amorphous thin-film dielectrics often result in defect-states or electronic traps. These traps are responsible for increased leakage currents and bulk charge trapping in many associated applications. Additional defects may be generated during regular usage, leading to electrical breakdown. Increased leakage currents, charge trapping and defect generation/breakdown are important and pervasive reliability concerns in amorphous dielectrics. We first explore the issue of charge accumulation and leakage in amorphous dielectrics. Historically, charge transport in amorphous dielectrics has been presumed, depending on the dielectric thickness, to be either bulk dominated (Frenkel-Poole (FP) emission) or contact dominated (Fowler-Nordheim tunneling). We develop a comprehensive dielectric charging modeling framework which solves for the transient and steady state charge accumulation and leakage currents in an amorphous dielectric, and show that for intermediate thickness dielectrics, the conventional assumption of FP dominated current transport is incorrect, and may lead to false extraction of dielectric parameters. We propose an improved dielectric characterization methodology based on an analytical approximation of our model. Coupled with ab-initio computed defect levels, the dielectric charging model explains measured leakage currents more accurately with lesser empiricism. We study RF-MEMS capacitive switches as one of the target applications of intermediate thickness amorphous dielectrics. To achieve faster analysis and design of RF-MEMS switches in particular, and electro-mechanical actuators in general, we propose a set of fundamental scaling relationships which are independent of specific physical dimensions and material properties; the scaling relationships provide an intrinsic classification of all electro-mechanical actuators. However, RF-MEMS capacitive switches are plagued by the reliability issue of temporal shifts of actuation voltages due to dielectric charge accumulation, often resulting in failure due to membrane stiction. Using the dielectric charging model, we show that in spite of unpredictable roughness of deposited dielectrics, there are predictable shifts in actuation voltages due to dielectric charging in RF-MEMS switches. We also propose a novel non-obtrusive, non-contact, fully electronic resonance based technique to characterize charging driven actuation shifts in RF-MEMS switches which overcomes limitations in conventionally used methods. Finally, we look into the issue of defect generation and breakdown in thick polymer dielectrics. Polymer materials often face premature electrical breakdown due to high electric fields and frequencies, and exposure to ambient humidity conditions. Using a field-driven correlated defect generation model, coupled with a model for temperature rise due to dielectric heating at AC stresses, we explain measured trends in time-to-breakdown and breakdown electric fields in polymer materials. Using dielectric heating we are able to explain the observed lifetime and dielectric strength reduction with increasing dielectric thicknesses. Performing lifetime measurements after exposure to controlled humidity conditions, we find that moisture ingress into a polymer material reduces activation barriers for chain breakage and increases dielectric heating. Overall, this thesis develops a comprehensive framework of dielectric charging, leakage and degradation of insulators of different thicknesses that have broad applications in multiple technologies.